不管是什么材料制作的手板模型，當它超出了一定的使用條件限制，可能就會出現手板模型變形或是裂紋，那么遇到手板模型產生變形或是裂紋應該怎么做?還有沒有方法可以補救?下面濟南手板加工廠就來給大家說說手板模型產生變形或是裂紋的補救措施，大家可以看看內容了解一下。

No matter what material is made of, when it exceeds a certain limit of use conditions, it may be deformed or cracked. What should we do when it is deformed or cracked? Is there any way to remedy it? Next, Jinan Handboard Processing Factory will tell you about the remedial measures for the deformation or crack of the handboard model. You can have a look at the contents.

1、手板發生變形后，其內部存在一定的殘余應力。在對手板加工前應該應力。可以使用應力退火和自然時效來使內部應力消失。

1. After the hand plate is deformed, there is a certain residual stress in it. The stress should be relieved before processing the hand plate. Stress annealing and natural aging can be used to eliminate internal stress.

2、手板熱裂紋多數是由于機械應力造成，是在金屬凝固所造成的裂紋。解決辦法是改良手板結構，使其與金屬接觸的面更少。另外一種辦法是在控制金屬的含硫量而增加金屬的熱脆性。

2. The hot cracks of the hand plate are mostly caused by mechanical stress and are caused by metal solidification. The solution is to improve the hand board structure so that it has less contact with metal. Another way is to control the sulfur content of the metal and increase the thermal brittleness of the metal.

3、手板冷裂紋是在低溫下所產品的裂紋。這是由于手板變形引致的，常常出現在手板受拉伸的地方，冷裂紋一般比較細小，但這種裂紋是不可逆的缺陷，只能重做。在制作大型而薄的手板時，常發生冷裂紋。相似，預防辦法也是減小內部應力和控制金屬中磷的含量。

3. The cold crack of the hand plate is the crack of the product at low temperature. This is caused by the deformation of the hand board, which often occurs in the place where the hand board is under tension. The cold crack is generally small, but this kind of crack is irreversible and can only be redone. When making large and thin hand boards, cold cracks often occur. Similarly, the preventive measures are to reduce the internal stress and control the content of phosphorus in the metal.

此外手板模型材料的選用，既要滿足客戶對產品質量的要求，還需考慮到材料的成本及其在設定周期內的強度，當然還要根據手板模型的類型、使用工作方式、加工速度、主要失效形式等因素來選材。

In addition, the selection of the material of the hand model should not only meet the customer's requirements for product quality, but also take into account the cost of the material and its strength within the set period. Of course, the material should be selected according to the type of the hand model, the working mode, the processing speed, the main failure forms and other factors.

例如：沖裁模的主要失效形式是刃口磨損，就要選擇表面硬度高、耐磨性好的材料；沖壓模主要承受周期性載荷，易引起表面疲勞裂紋，導致表層剝落，那就要選擇表面韌性好的材料；拉深模應選擇磨擦系數特別低的材料。

For example, the main failure form of blanking die is edge wear, so it is necessary to select materials with high surface hardness and good wear resistance; Stamping die mainly bears periodic load, which is easy to cause surface fatigue crack and lead to surface peeling, so it is necessary to select materials with good surface toughness; The drawing die shall be made of materials with low friction coefficient.

可以看出一旦手板模型發生變形和裂紋，補救措施非常麻煩，甚有些變形和裂紋是無法補救的，是手板模型的重大缺陷，所以變形和裂紋是以預防措施為主，盡量避免出現變形和裂紋。更多相關內容就來我們網站http://www.seaoil.cn咨詢了解吧！

It can be seen that once deformation and cracks occur in the hand model, remedial measures are very troublesome, and even some deformation and cracks cannot be remedied, which are major defects of the hand model. Therefore, deformation and cracks are mainly preventive measures to avoid deformation and cracks as much as possible. Come to our website for more relevant content http://www.seaoil.cn Ask about it!